Hydrogenated In-doped ZnO Thin Films for the New Anode Material of Organic Light Emitting Devices: Synthesis and Application Test
Donggeun Jung1  Young Ran Park1  Young Sung Kim1  Eunkyoung Nam1  Su Jeong Suh1  Jin-Hyo Boo1 
关键词: Indium doped zinc oxide (IZO);    Hydrogen effect;    Organic light emitting diodes (OLEDs);    Pulsed DC magnetron sputtering;    Transparent conducting oxide;   
DOI  :  
学科分类:化学(综合)
来源: Korean Chemical Society
PDF
【 摘 要 】

Transparent In-doped (1 at.%) zinc oxide (IZO) thin films are deposited by pulsed DC magnetron sputtering with H2 mixed Ar atmosphere on glass substrate without any heating process. Even at room temperature, highly c-axis oriented IZO thin films were grown in perpendicular to the substrate. The hydrogenated IZO (IZO:H) film isolated in H2 atmosphere for 30 min exhibited an average optical transmittance higher than 85% and low electrical resistivity of less than 2.7 �? 10?3 ヘ·cm. These values are comparable with those of commercially available ITO. Each of the IZO films was used as an anode contact to fabricate organic light-emitting diodes (OLEDs) and the device performances studied. At the current density of 1 �? 103 A/m2, the OLEDs with IZO:H (H2) anode show excellent efficiency (11 V drive voltage) and a good brightness (8000 cd/m2) of the light emitted from the devices, which are as good as the control device built on a commercial ITO anode.

【 授权许可】

Unknown   

【 预 览 】
附件列表
Files Size Format View
RO201912010240358ZK.pdf 923KB PDF download
  文献评价指标  
  下载次数:5次 浏览次数:5次