Influence of boron doping on mechanical and tribological properties in multilayer CVD-diamond coating systems

Bulletin of materials science

S BALAJI³  SAJAD HUSSAIN DIN²  M S RAMACHANDRA RAO³  K A NAJAR¹  M A SHAH⁴  N A SHEIKH¹  K RAMASUBRAMANIAN³ 

[1] Department of Mechanical Engineering, National Institute of Technology, Srinagar 190006, India$$Department of Mechanical Engineering, National Institute of Technology, Srinagar 190006, IndiaDepartment of Mechanical Engineering, National Institute of Technology, Srinagar 190006, India$$;Department of Mechanical Engineering, National Institute of Technology, Srinagar 190006, India$$Department of Physics, National Institute of Technology, Srinagar 190006, India$$Department of Mechanical Engineering, National Institute of Technology, Srinagar 190006, IndiaDepartment of Mechanical Engineering, National Institute of Technology, Srinagar 190006, India$$Department of Physics, National Institute of Technology, Srinagar 190006, India$$Department of Physics, National Institute of Technology, Srinagar 190006, IndiaDepartment of Mechanical Engineering, National Institute of Technology, Srinagar 190006, India$$Department of Physics, National Institute of Technology, Srinagar 190006, India$$;Nano Functional Materials Technology Centre, Department of Physics, Indian Institute of Technology Madras, Chennai 600036, India$$Nano Functional Materials Technology Centre, Department of Physics, Indian Institute of Technology Madras, Chennai 600036, IndiaNano Functional Materials Technology Centre, Department of Physics, Indian Institute of Technology Madras, Chennai 600036, India$$;Department of Physics, National Institute of Technology, Srinagar 190006, India$$Department of Physics, National Institute of Technology, Srinagar 190006, IndiaDepartment of Physics, National Institute of Technology, Srinagar 190006, India$$

关键词: Boron doping;    multilayer CVD-diamond coatings;    nano-indentation;    Al$_2$O$_3$;    hardness;    friction coefficient.;   

DOI  :  

学科分类：材料工程

来源: Indian Academy of Sciences

【 摘 要 】

Titanium alloy (Ti6Al4V) substrates were deposited with smooth multilayer coatings, by hot filament chemical vapour deposition technique. The effect of boron doping on lattice parameter, residual stresses, hardness and coefficient of friction in multilayer-diamond coating system was studied. The frictional behaviour of the coatings was studied using a ball-on-disc micro-tribometer by sliding the coated samples of titanium alloy (Ti6Al4V) substrates against alumina (Al$_2$O$_3$) balls, and increasing normal load from 1 to 10N. The average friction coefficient decreased from 0.36 to 0.29 for undoped multilayer-diamond coating system and from 0.33 to 0.18 for borondoped (BD) multilayer-diamond coating system. The average indentation depths for undoped and BD multilayerdiamond coating systems were found to be equal to $sim$58 and $sim$65 nm, respectively, and their hardness values were 60 and 55~GPa, respectively.