Synthesis and characterization of mesoporous Si-MCM-41 materials and their application as solid acid catalysts in some esterification reactions

Bulletin of materials science

Tarun F Parangi¹  Uma V Chudasama¹  Rajesh M Patel¹ 

[1] Applied Chemistry Department, Faculty of Technology and Engineering, M.S. University of Baroda, Vadodara 390 001, India$$Applied Chemistry Department, Faculty of Technology and Engineering, M.S. University of Baroda, Vadodara 390 001, IndiaApplied Chemistry Department, Faculty of Technology and Engineering, M.S. University of Baroda, Vadodara 390 001, India$$

关键词: Mesoporous material;    Si-MCM-41;    Al-MCM-41;    heteropoly acid anchored onto MCM-41;    esterification;    solid acid catalyst.;   

DOI  :  

学科分类：材料工程

来源: Indian Academy of Sciences

【 摘 要 】

Mesoporous MCM-41 has been synthesized by solâ€�?�gel method at room temperature possessing good thermal stability, high surface area as well as retention of surface area at high temperature. The MCM-41 neutral framework has been modified and put to practical use by incorporating Al³⁺ in the siliceous MCM-41 framework and supporting 12-TPA (12-tungstophosphoric acid) onto MCM-41 by process of anchoring and calcination to induce Brønsted acidity in MCM-41 to yield Al-MCM-41 and 12TPA-MCM-41, respectively. The synthesized materials have been characterized for elemental analysis by ICP-AES, XRD, SEM, TEM, EDX, FTâ€�?�IR and TGA. Surface area has been determined by BET method and pore size and pore size distribution determined by BJH method. Surface acidity has been evaluated by NH₃-TPD method. The potential use of Al-MCM-41 and 12TPA-MCM-41 as solid acid catalysts has been explored and compared by studying esterification as a model reaction wherein monoesters such as ethyl acetate (EA), propyl acetate (PA), butyl acetate (BA) and benzyl acetate (BzA) have been synthesized, optimizing several parameters such as catalyst amount, reaction time, reaction temperature and mole ratio of reagents.