Poisoning effect of bismuth on modification behaviour of strontium in LM25 alloy

Bulletin of materials science

A Ourdjini¹  S Farahany¹  M H Idris¹  L T Thai¹ 

[1] Materials Engineering Department, Faculty of Mechanical Engineering, UTM Skudai, 81310 Johor, Malaysia$$Materials Engineering Department, Faculty of Mechanical Engineering, UTM Skudai, 81310 Johor, MalaysiaMaterials Engineering Department, Faculty of Mechanical Engineering, UTM Skudai, 81310 Johor, Malaysia$$

关键词: Thermal analysis;    bismuth;    modification;    aluminium alloy.;   

DOI  :  

学科分类：材料工程

来源: Indian Academy of Sciences

【 摘 要 】

Nucleation and growth, temperature measurements andmicrostructure observations of silicon phase are presented for strontium modified Al�??7%Si (LM25) cast alloy treated with bismuth. The results show that addition of bismuth in strontium modified alloys may have a poisoning effect resulting in lost modification of the silicon phase. With increasing Bi/Sr ratio, thermal analysis measurements showed that the eutectic growth temperature increased remarkably to 573°C and recalescence decreased to 0.2°C and the morphology of silicon displayed the same flakelike structure as in the unmodified alloys. Microstructural observation showed that a minimum Bi/Sr ratio of 1.2 which is equivalent to a Sr/Bi ratio of 0.43 is required for effective strontium modification and neutralization of the poisoning effect of bismuth.

【 授权许可】

Unknown