Evaluation of a.c. conductivity of rubber ferrite composites from dielectric measurements

Bulletin of materials science

S Sindhu¹  K A Malini¹  M R Anantharaman¹  Philip Kurian²  Bindu P Thampi¹ 

[1] Department of Physics, Cochin University of Science and Technology, Cochin 682 022, India$$Department of Physics, Cochin University of Science and Technology, Cochin 682 022, IndiaDepartment of Physics, Cochin University of Science and Technology, Cochin 682 022, India$$;Department of Polymer Science and Rubber Technology, Cochin University of Science and Technology, Cochin 682 022, India$$Department of Polymer Science and Rubber Technology, Cochin University of Science and Technology, Cochin 682 022, IndiaDepartment of Polymer Science and Rubber Technology, Cochin University of Science and Technology, Cochin 682 022, India$$

关键词: Rubber ferrite composites;    a.c. electrical conductivity;    mixed ferrites;    electrical properties;    magnetic materials;    polymer magnets.;   

DOI  :  

学科分类：材料工程

来源: Indian Academy of Sciences

【 摘 要 】

The effect of frequency, composition and temperature on the a.c. electrical conductivity were studied for the ceramic, Ni_{1â€�?�ð�?��?}Zn_ð‘�?Fe₂O₄, as well as the filler (Ni_{1â€�?�ð�?��?}Zn_ð‘�?Fe₂O₄) incorporated rubber ferrite composites (RFCs). Ni_{1â€�?�ð�?��?}Zn_ð‘�?Fe₂O₄ (where ð‘�? varies from 0 to 1 in steps of 0.2) were prepared by usual ceramic techniques. They were then incorporated into a butyl rubber matrix according to a specific recipe. The a.c. electrical conductivity (𝜎_a.c.) calculations were carried out by using the data available from dielectric measurements and by employing a simple relationship. The a.c. conductivity values were found to be of the order of 10^â€�??3 S/m. Analysis of the results shows that 𝜎_a.c. increases with increase of frequency and the change is same for both ceramic Ni_{1â€�?�ð�?��?}Zn_ð‘�?Fe₂O₄ and RFCs. 𝜎_a.c. increases initially with the increase of zinc content and then decreases with increase of zinc. Same behaviour is observed for RFCs too. The dependence of 𝜎_a.c. on the volume fraction of the magnetic filler was also studied and it was found that the a.c. conductivity of RFCs increases with increase of volume fraction of the magnetic filler. Temperature dependence of conductivity was studied for both ceramic and rubber ferrite composites. Conductivity shows a linear dependence with temperature in the case of ceramic samples.