Role of some rare earth (RE) ions (RE = La, Pr, Nd, Sm, Gd and Dy) in crystal and mechanical behaviours of sol�?�gel derived ZrO2�??2 mol% RE2O3 spun fibres calcined at 1300°C | |
D Ganguli1  M Chatterjee2  M K Naskar2  | |
[1] Sol�?�Gel Division, Central Glass and Ceramic Research Institute, Kolkata 700 032, India$$Department of Materials Science, Indian Association for the Cultivation of Science, Kolkata 700 032, India$$Sol�?�Gel Division, Central Glass and Ceramic Research Institute, Kolkata 700 032, IndiaSol�?�Gel Division, Central Glass and Ceramic Research Institute, Kolkata 700 032, India$$Department of Materials Science, Indian Association for the Cultivation of Science, Kolkata 700 032, India$$Department of Materials Science, Indian Association for the Cultivation of Science, Kolkata 700 032, IndiaSol�?�Gel Division, Central Glass and Ceramic Research Institute, Kolkata 700 032, India$$Department of Materials Science, Indian Association for the Cultivation of Science, Kolkata 700 032, India$$;Sol�?�Gel Division, Central Glass and Ceramic Research Institute, Kolkata 700 032, India$$Sol�?�Gel Division, Central Glass and Ceramic Research Institute, Kolkata 700 032, IndiaSol�?�Gel Division, Central Glass and Ceramic Research Institute, Kolkata 700 032, India$$ | |
关键词: Rare earth; ionic size; crystallization temperature; phase transformation; lattice strain; tensile strength.; | |
DOI : | |
学科分类:材料工程 | |
来源: Indian Academy of Sciences | |
【 摘 要 】
Crystal behaviours such as crystallization temperature (amorphous to tetragonal (�) zirconia), tendency of phase transformation (tetragonal to monoclinic (�) zirconia) and lattice strain were studied with mechanical property e.g. tensile strength of sol�?�gel derived ZrO2�??2 mol% RE2O3 (RE = La, Pr, Nd, Sm, Gd and Dy) spun fibres. Rare earth cations of varying sizes played a significant role in changing the above mentioned properties of ZrO2�??2 mol% RE2O3 fibres. It was found that with decreasing the ionic size difference between the zirconium and RE ions, crystallization temperature (amorphous $ightarrowt$-ZrO2) decreased, the probability of phase transformation ($t ightarrow m$) decreased, lattice strain which is related to lattice distortion decreased and tensile strength increased.