Effect of ball milling times on phase formation of Mg0.7Zn0.3Fe2O4 | Science Publications | |
Panuthat Khotsongkram1  Aurawan Rittidech1  | |
关键词: Mg0.7Zn0.3Fe2O4; ball-milling; calcination; | |
DOI : 10.3844/ajassp.2006.1760.1762 | |
学科分类:自然科学(综合) | |
来源: Science Publications | |
【 摘 要 】
Mg0.7Zn0.3Fe2O4 (MZF) powder was prepared by a solid-state mixed oxide using ball-milling technique. The phase identification of calcined powders was performed using X-ray diffraction technique (XRD). It has been found that MZF powders were successfully obtained for calcination conditions of 800 oC for milling times of 36 h, whereas milling times of 12 h, unreacted ZnO, Fe2O3 and MgO phases (2θ ~ 54, 57 and 63) are detected from the original mixture up to 900 oC. By increasing the calcination temperature to 1000 oC, a single phase of MZF is formed. Moreover, the microstructure of powder were examined by scanning electron microscopy (SEM) and showed that the particle in size from 58-1200 nm. While, XRD patterns were obtained average size of particle, calculation by Scherrer's equation,between 30.54 - 66.59 nm.
【 授权许可】
Unknown
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO201911300938459ZK.pdf | 587KB | download |