Crack growth through low-cycle fatigue loading of material ARMOX 500T

Metalurgija

Kunc, R.¹  Prebil, I.¹  Žerovnik, A.¹  Pepel, V.¹ 

[1] University of Ljubljana, Faculty of Mechanical Engineering, Ljubljana, Slovenia

关键词: steel Armox 500T;    low-cycle fatigue;    crack growth;    damage;    structure;   

DOI  :  

学科分类：金属与冶金

来源: Hrvatsko Metalursko Drustvo

【 摘 要 】

This paper presents microstructure analysis of the creation and growth of cracks in uniaxial load. Analyse were done for steel Armox 500T (armour sheet). Results show that cracks are present quit early in steel lifetime. First micro...