Enhanced dielectric and piezoelectric properties in microwave sintered (Ba$_{0.997}$Nd$_{0.003}$)TiO$_3$ ceramic when compared to conventional sintered ceramics | |
RIZWANA^21  S MAHBOOB^12  | |
[1] Institute of Aeronautical Engineering, Dundigal, Hyderabad 500043, India^2;Materials Research Laboratory, Department of Physics, Osmania University, Hyderabad 500007, India^1 | |
关键词: (Ba$_{0.997}$Nd$_{0.003}$)TiO$_3$ ceramic; microwave sintering; dielectric; conductivity; impedance; piezoelectric.; | |
DOI : | |
学科分类:材料工程 | |
来源: Indian Academy of Sciences | |
【 摘 要 】
Dielectric, conductivity and piezoelectric properties have been studied on (Ba$_{0.997}$Nd$_{0.003}$)TiO$_3$ ceramic samples prepared through microwave sintered (MWS) and conventional sintered (CS) routes and the results are presented in this paper. The room temperature dielectric constant at 10 kHz for CS and MWS samples are 1245 and 5250 respectively. Roomtemperature dielectric constant in MWS sample was almost four times higher than that of the CS sample. The value of $K_t$ is found to be 0.998 and 0.997; whereas the value of $d_{33}$ is 7.72 nm V$^{â1}$ (573 K) and 444.66 nm V$^{â1}$ (573 K) for CS and MWS samples, respectively. In the present study almost 57 times enhancement in piezoelectric charge constant ($d_{33}$) isobserved for the MWS Ba$_{0.997}$Nd$_{0.003}$TiO$_3$ ceramic when compared to the CS ceramic.