Reconfiguration of Point Defects in FCC and HCP Metals at Initial Stage of Recovery Process/ Rekonfiguracja Struktury Defektów Sieciowych W Początkowym Stadium Zdrowienia Metali O Sieci Rsc I Hz

Archives of Metallurgy and Materials

G. Boczkal¹  M. Perek-Nowak¹ 

[1] AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, FACULTY OF NON-FERROUS METALS, AL. A. MICKIEWICZA 30, 30-059 KRAKÓW, POLAND

关键词: Keywords : FCC metals;    HCP metals;    point defects;    resistivity measurements;   

DOI  :  10.2478/amm-2014-0225

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The conducted studies regarded the analysis of change of structure of point defects occurring during initial stage of recovery of FCC (Al, Cu) and HCP (Ti, Mg and Zn) metals at temperature close to Th =0.5Tm. The changes in resistivity of the deformed and later recovered samples were measured. The recovery time was 1, 2, 3, 4 or 5 min. The observed changes were correlated with reorganization of arrangement of lattice defects during annealing.