Atmosphere Effect on Sintering Behaviour of Astaloy CrM and Astaloy CrL Höganäs Powders with Manganese and Carbon Additions / Wpływ Atmosfery Na Spiekalność Komercyjnych Proszków Höganäs Astaloy CrM I Astaloy CrL Z Dodatkami Manganu I Węgla

Archives of Metallurgy and Materials

A. Ciaś¹  M. Sułowski¹  T. Pieczonka¹ 

[1] AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, FACULTY OF METALS ENGINEERING AND INDUSTRIAL COMPUTER SCIENCE, 30-059 KRAKÓW, 30 MICKIEWICZA AV., POLAND

关键词: Keywords: pre-alloyed iron based powders;    sintering;    dimensional control;    dilatometry;   

DOI  :  10.2478/v10172-012-0112-6

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

Dilatometric data for Astaloy CrM (3% Cr-0.5% Mo) and Astaloy CrL (1.5% Cr-0.2% Mo) powders with additions of 0.3% carbon and 3.0% manganese during sintering cycles up to 1120 and 1250°C in different atmospheres are reported. For comparison, also Astaloy CrM and Astaloy CrL powders were investigated. Starting with green densities of approx. 6.8 g/cm3, the final density of sintered compacts was influenced mainly by the sintering temperature, while the results showed the only minor effect of the sinteringatmosphere on the final dimensional changes. However, the sintering atmosphere influences the sintering behaviour, microstructure and the final chemical composition of sintered compacts. In sintered and in the dilatometer cooled Mn-Cr-Mo-C steels predominantly bainitic structures were obtained.