A study on structural stability of bismuth titanate with lanthanum doping for improved ferroelectric properties

Bulletin of Materials Science

关键词: Bi$_4$Ti$_3$O$_{12}$;    lanthanum;    oxygen vacancies;    ferroelectric.;   

学科分类：材料工程

来源: Indian Academy of Sciences

【 摘 要 】

Bismuth titanate (Bi$_4$Ti$_3$O$_{12}$) with different lanthanum (La) concentrations (0.25, 0.50, 0.75 and 1.0 mol%) was successfully prepared via soft combustion route. It was found that the change of diffraction peaks shown by X-ray diffraction is attributed to the doping effect in Bi$_4$Ti$_3$O$_{12}$. This was also supported by the presence of additional peak that correspondsto La in the range of 800–860 eV, proved by X-ray photoelectron spectroscopy. In addition, the enlarged region of Bi 4f, Bi 4d, Ti 2p, La 3d and O 1s of doping sample was clearly seen after deconvolution. Based on binding energy position, it can be unambiguously stated that the Ti ions in the tetravalent state are surrounded by the perovskite layer of Bi$_4$Ti$_3$O$_{12}$, whichmay also imply the formation of oxygen vacancies in the vicinity of the Bi$_2$O$_2$ layer. In comparison with Bi$_4$Ti$_3$O$_{12}$, thegreen emission intensity was abruptly decreased with La doping. This indicates that La doping suppresses the formation of oxygen vacancies by stabilizing the adjacent oxide ions. Thus, the improved polarization shown by ferroelectric hysteresis loop is associated with the reduction in oxygen and bismuth vacancies due to La doping.

【 授权许可】

CC BY