Repair Welding of SQV2A Pressure Vessel Steel by Temper Bead Techniques Without Post Welding Heat Treatment

Archives of Metallurgy and Materials

M. Łomozik¹  F. Matsuda²  R. Mizuno²  P. Brziak³ 

[1] Institute of Welding, 44-100 Gliwice, 16-18 B?. Czes?Awa Str., Poland;NDE Center, Japan Power Engineering and Inspection Corporation (Japeic), Yokohama, Japan;Welding Research Institute - Industrial Institute of Se, Bratyslava, Slovakia

关键词: Keywords: thermal welding cycle;    HAZ;    heat treatment;    temper bead welding;   

DOI  :  10.2478/v10172-011-0024-x

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

SQV2A Manganese-Molybdenum-Nickel ferritic steel has been developed for pressure vessel fabrication. Due to its chemical composition and carefully controlled heat treatment the SQV2A steel consists of fine-grained tempered martensite/lower bainite microstructure, which exhibits well-balanced combination of strength and low temperature toughness. However, this balance is disturbed by the thermal cycles experienced during welding, producing areas of unaccepted mechanical behaviors. Generally, a decrease in toughness of some regions of BM Heat Affected Zone is the most critical aspect of multi-layer (repair) welding. A full scale Post Welding Heat Treatment (PWHT) usually restores the mechanical behaviors to requested levels. Additionally, PWHT removes hydrogen trapped in the microstructure during welding. A situation becomes critical, when on-site local (repair) welding takes place. Harsh environment, difficult access and a presence other facilities make the in-situ PWHT almost inapplicable. In term of cold cracking prevention, a Gas Tungsten arc Welding (GTAW) gives acceptable hydrogen levels in the weld region; and full scale PWHT is unnecessary. This is the main reason why the GTAW has become a leading process for on-site (repair) welding of heavy section components. Moreover, a automatic GTAW process offers better weld geometry controlling which has become out of importance for welding not followed by PWHT. A precisely controlled multiple weld thermal cycles of predefined peak temperatures in particular weld regions can be employed for restoring the mechanical behavior of critical weld areas instead of full scale PWHT.