Welding of Thermomechanically Rolled Fine-Grain Steel by Different Types of Lasers/ Spawanie Stali Drobnoziarnistej Walcowanej Termomechanicznie Laserami Różnego Typu

Archives of Metallurgy and Materials

A. Lisiecki¹ 

[1] SILESIAN UNIVERSITY OF TECHNOLOGY, WELDING DEPARTMENT, 18A KONARSKIEGO STR., 44-100 GLIWICE, POLAND;

关键词: Keywords: laser;    welding;    keyhole;    thermomechanically rolled;    fine-grain steel;   

DOI  :  10.2478/amm-2014-0276

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The autogenous laser welding of 2.5 mm thick butt joints of thermomechanically rolled fine-grain steel grade S420MC was investigated. Butt joints were laser welded by the Yb:YAG Disk laser, emitted a circular laser beam with spot diameter of 200 μm at 1.03 μm wavelength, and also by the high power direct diode laser, emitted a rectangular beam with dimension of 1.8x6.8 mm at 808 nm wavelength. Different welding modes were identified for the lasers applied. The conduction welding mode was observed in whole of the diode laser welding parameters. While high quality joints, without any internal defects and characterized with satisfactory mechanical performance were produced in a wide range of parameters. The butt joints produced by Disk laser were welded at keyhole mode. In this case a slight tendency to weld porosity was found.