The Defects of Oxide Layers Formed on 10CrMo9-10 Steel Operated for 200,000 Hours at an Elevated Temperature

Archives of Metallurgy and Materials

M. Gwoździk¹ 

[1] CZESTOCHOWA UNIVERSITY OF TECHNOLOGY, THE FACULTY OF PRODUCTION ENGINEERING AND MATERIALS TECHNOLOGY, 19 ARMII KRAJOWEJ AV., 42-200 CZESTOCHOWA, POLAND;

关键词: Keywords: oxide layer;    10CrMo9-10 steel;    LM;    SEM;    AFM;    XRD;   

DOI  :  10.1515/amm-2016-0168

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The paper contains results of studies into the formation of oxide layers on 10CrMo9-10 (10H2M) steel long-term operated at an elevated temperature (T = 545°C, t = 200,000h). The oxide layer was studied on a surface and a cross-section at the inner and outer surface of the tube wall on the outlet both on the fire and counter-fire side of the tube wall surface.