Fabrication Of Porous Ti By Thermal Decomposition And Sintering Of PMMA/TiH2 Powder Compact

Archives of Metallurgy and Materials

M.-J. Suk¹  Y.D. Kim²  S.-T. Oh³  K.Ch. Jeon³ 

[1] DEPARTMENT OF MATERIALS AND METALLURGICAL ENGINEERING, KANGWON NATIONAL UNIVERSITY, SAMCHEOK 245-711, KOREA;DEPARTMENT OF MATERIALS SCIENCE AND ENGINEERING, HANYANG UNIVERSITY, SEOUL 133-791, KOREA;DEPARTMENT OF MATERIALS SCIENCE AND ENGINEERING, SEOUL NATIONAL UNIVERSITY OF SCIENCE AND TECHNOLOGY, SEOUL 139-743, KOREA

关键词: Keywords: Porous Ti;    PMMA powders;    Thermal decomposition of TiH2;    Pore structure;   

DOI  :  10.1515/amm-2015-0134

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

Porous Ti with controlled pore structure was fabricated by thermal decomposition and sintering process using TiH2 powders and Polymethylmethacrylates (PMMA) beads as pore forming agent. The beads sizes of 8 and 50 μm were used as a template for fabricating the porous Ti. The TiH2 powder compacts with 20 and 70 vol% PMMA were prepared by uniaxial pressing and sintered for 2 h at 1100°C. TGA analysis revealed that the PMMA and TiH2 were thermally decomposed at about 400°C forming pores and at about 600°C into metallic Ti phase. The porosity increased with increase in the amount of PMMA addition. Also, the microstructure observation showed that the pore size and shape were strongly dependent on the PMMA shapes.