Analysis of Crystallite Size and Lattice Deformations Changes in an Oxide Layer on P91 Steel / Analiza Zmian Wielkosci Krystalitów I Odkształcen Sieciowych W Warstwie Tlenków Na Stali P91

Archives of Metallurgy and Materials

M. Gwozdzik¹  Z. Nitkiewicz¹ 

[1] CZESTOCHOWA UNIVERSITY OF TECHNOLOGY, INSTITUTE OF MATERIALS ENGINEERING, 42-201 CZESTOCHOWA, 19 ARMII KRAJOWEJ AV., POLAND

关键词: Keywords: crystallite sizes;    P91 steel;    oxide layers;   

DOI  :  10.2478/v10172-012-0146-9

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The paper contains results of studies on X-ray diffraction analysis XRD (studying the phase composition, crystallite sizes and lattice deformations) of oxide layers on P91 steel, operated for a long time at an elevated temperature (T = 535°C, t = 70,000 h). X-ray studies were carried out on the inner surface of a tube, and then the layer surface was polished down to 3.5 μm and the diffraction measurements were performed again to determine individual oxide layers. It has been found that a three-zone oxide layer is formed as a result of long-term operation of P91 steel at the temperature of 535°C. Hematite occurs on the inner surface of the tube. Then magnetite appears below hematite. Going deeper into the layer there is a spinel, i.e. a mixture of magnetite and chromite. A visible decay of total intensity for Fe2O3 is observed already at the polishing depth of 3.5 μm. In the case of Fe3O4 and FeCr2O4 an increase in total intensity is observed already from 7 μm, what manifests in narrowing the diffraction line and hence in increasing the crystallites size and in the relaxation of stresses in this oxide layer. The broadening of a diffraction line caused by a small size of crystallites is expressed by the Scherrer relationship. Instead, the β2 broadening resulting from lattice distortions (relaxation of stresses) was determined from the Taylor relationship.