期刊论文详细信息
Bulletin of Materials Science
Electromagnetic interference shielding effectiveness of MgO−Al$_2$O$_3$−SiO$_2$ glass–ceramic system
关键词: Microwave shielding;    glass–ceramics;    nucleating agent.;   
学科分类:材料工程
来源: Indian Academy of Sciences
PDF
【 摘 要 】

MgO−Al$_2$O$_3$−SiO$_2$ (MAS)-based glass–ceramic system was prepared using very-low-cost raw materials, i.e.,talc, calcined alumina and calcined china clay with titanium dioxide as a nucleating agent. Glass–ceramics were preparedby a two-step process. In the first step, raw materials were mixed in the required proportion and melted at 1450$^{\circ}$C followedby water quench into a glassy frit. In the second step, powdered glass frit was uniaxially dry pressed into pellets followedby sintering at 1200$^{\circ}$C for 3h. X-ray diffraction pattern of the sintered compact shows well-defined peaks of cordieritealong with some anorthite and magnesium titanium oxide. The microstructure study of sample shows the presence of crystallineand glassy phases. Permittivity and permeability measurements were performed in the microwave frequency range12.4–17 GHz. The permittivity value of 5.7–6.0 and the permeability value of $\sim$1 were obtained. The reflection and transmission measurements show that the material possesses a shielding effectiveness in the range 2–10 dB over the frequencyrange 12.4–17 GHz.

【 授权许可】

CC BY   

【 预 览 】
附件列表
Files Size Format View
RO201902182019308ZK.pdf 152KB PDF download
  文献评价指标  
  下载次数:16次 浏览次数:19次