Mechanical Spectroscopy of MgB2 Containing Sic / Spektroskopia Mechaniczna MgB2 Zawierającego Sic

Archives of Metallurgy and Materials

C.R. Grandini¹  M.R. Silva¹  D. Rodrigues Junior²  L.B.S. Silva² 

[1] UNESP - Univ. Estadual Paulista , Laboratório de Anelasticidade e Biomateriais , 17.033-360, Bauru, SP, Brazil;USP, Laboratório de Materiais Especiais, 12.602-810, Lorena, SP, Brazil

关键词: Keywords: Mechanical spectroscopy;    internal friction;    anelasticity;    MgB2;    SiC;   

DOI  :  10.1515/amm-2015-0492

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The compound magnesium diboride (MgB2) has been well-known since the 1950s; however, its superconducting properties were unknown. Intrinsic characteristics of MgB2 make this material a promising candidate for technological applications, although the low value of the irreversibility field and the decrease in critical current density with the increase in the magnetic field considerably reduce its utility. The present work aimed to study the effect of carbon-based doping on anelastic properties of MgB2 as measured by mechanical spectroscopy. The samples were prepared by using the powder-intube method. The samples were made with 5, 7.5, and 10 wt.% of silicon carbide (SiC). The results reveal complex mechanical loss spectra caused by the interaction between point defects and surface defects in the crystalline lattice of MgB2.