Enhanced high temperature performance of LiMn2O4 coated with Li3BO3 solid electrolyte
关键词: Lithium ion battery;    lithium manganese oxide;    coating;    solid-state method.;   
学科分类:材料工程
来源: Indian Academy of Sciences
PDF
【 摘 要 】

Cathode material, LiMn2O4, was synthesized by solid-state reaction followed by surface coating of Li3BO3 solid electrolyte. Structure and electrochemical performance of the prepared powders were characterized by X-ray diffraction, scanning electron microscopy, cyclic voltammetry, electrochemical impedance spectroscopy and galvanostatic charge–discharge techniques, respectively. Results show that Li3BO3 coated LiMn2O4 has similar X-ray diffraction patterns as LiMn2O4. The discharge specific capacities of LiMn2O4 coated with 0.1, 0.3 and 0.6 wt% Li3BO3 are 123.3, 118.2 and 110 mAh/g, respectively, which is slightly smaller than that of 124.4 mAh/g for LiMn2O4. However, the capacity retention of Li3BO3 coated LiMn2O4 is at least 5.6 and 7.6% higher than LiMn2O4 when cycled at room temperature and 55 °C, respectively. Li3BO3 coated LiMn2O4 shows much better cycling behaviours than LiMn2O4.

【 授权许可】

CC BY   

【 预 览 】
附件列表
Files Size Format View
RO201902181857200ZK.pdf 412KB PDF download
  文献评价指标  
  下载次数:10次 浏览次数:11次