Dependence Of The Structure And Magnetic Properties Of Cast Plate-Shaped Nd60Fe30Al10 Samples On Their Thickness

Archives of Metallurgy and Materials

P. Pawlik¹  W. Kaszuwara²  J. Latuch²  B. Michalski² 

[1] CZESTOCHOWA UNIVERSITY OF TECHNOLOGY, INSTITUTE OF PHYSICS, CZESTOCHOWA, 19 ARMII KRAJOWEJ AV., 42-200 CZESTOCHOWA, POLAND;WARSAW UNIVERSITY OF TECHNOLOGY, FACULTY OF MATERIALS SCIENCE AND ENGINEERING, 141WO?OSKA STR., 02-507 WARSZAWA, POLAND

关键词: Keywords: hard magnetic materials;    Nd-Fe-Al alloys;    rapid quenching;   

DOI  :  10.1515/amm-2015-0283

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The hard magnetic Nd-Fe-Al alloys are inferior to Nd-Fe-B magnets as far as the magnetic properties are concerned, but their great advantage is that they need no additional annealing to achieve good magnetic properties. These properties depend on the cooling rate from the melting state, and on the thickness of the sample - the best values are achieved at the quenching rates at which the samples have a thickness of 0.3-2 mm. The present study is concerned with the correlation between the magnetic properties of the plate-shaped Nd60Fe30Al10 samples and their size - thickness. Two casting ways: with the melt stream perpendicular direction and parallel to the surface of the plates were used. The plates were produced by pressure casting and suction casting. The studies have shown that the cooling rates depends on local propagation on liquid metal in the mold resulting in heterogeneity of structure and properties.