The use of Weibull Statistics to Quantify Property Variability in Fe-3Mn-0.8C Sinter-Hardened Structurally Inhomogeneous Steels
A. Czarski1  A. Cias1 
[1] AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, FACULTY OF METAL ENGINEERING AND INDUSTRIAL COMPUTER SCIENCE, DEPARTMENT OF PHYSICAL METALLURGY AND POWDER METALLURGY, AL. A. MICKIEWICZA 30, 30-059 KRAKÓW, POLAND
关键词: Keywords: strength of sintered steels;    Weibull statistics;    goodness of fit tests;   
DOI  :  10.2478/amm-2013-0124
学科分类:金属与冶金
来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy
PDF
【 摘 要 】

Low carbon ferro-manganese and graphite powders were admixed to Hoganas sponge, NC100.24, and water atomised, ABC 100.30 and ASC 100.29, iron powders - to produce three variants of sintered Fe-3Mn-0.8C steel. These were pressed into tensile and bend specimens at 660 MPa, sintered in semi-closed containers for 1 hour in dry nitrogen or hydrogen at 1120 or 1250°C and cooled at 64°C/min. Both tensile strength and transverse rupture strength were examined using Weibull statistics. This paper presents the results of a study to develop and evaluate goodness of fit tests for the two- and three-parameter Weibull distributions. The study was initiated because of discrepancies in published critical values for two-parameter Weibull distribution goodness of fit tests and the lack of general three-parameter Weibull distribution goodness of fit tests for properties of PM steels.