Archives of Metallurgy and Materials | |
Determination of γ′+γ / γ Phase Boundary in Ni-Al-Cr System Using DTA Thermal Analysis | |
K. Rzyman1  T. Maciąg1  | |
[1] Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, Institute of Metals Technology, 8 Krasinskiego Str., 40-019 Katowice, Poland | |
关键词: Keywords: DTA thermal analysis; order-disorder transition; Ni3Al; Ni-Al-Cr; | |
DOI : 10.1515/amm-2016-0044 | |
学科分类:金属与冶金 | |
来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy | |
【 摘 要 】
Mechanical properties at elevated temperature, in modern alloys based on intermetallic phase Ni3Al are connected with phase composition, especially with proportion of ordered phase γ′ (L12) and disordered phase γ (A1). In this paper, analysis of one key systems for mentioned alloys - Ni-Al-Cr, is presented. A series of alloys with chemical composition originated from Ni-rich part of Ni-Al-Cr system was prepared. DTA thermal analysis was performed on all samples. Based on shape of obtained curves, characteristic for continuous order-disorder transition, places of course of phase boundaries γ′+γ / γ were determined. Moreover, temperature of melting and freezing of alloys were obtained. Results of DTA analysis concerning phase boundary γ′+γ / γ indicated agreement with results obtained by authors using calorimetric solution method.