Welded Joint Cracking in Martensitic Stainless Steel Precipitation-Sthregthened with Copper / Pękanie Złącz Spawanych Stali Nierdzewnej Martenzytycznej Utwardzanej Wydzieleniowo Miedzią | |
E. Tasak1  A. Ziewiec1  J. Czech2  | |
[1]AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, FACULTY OF METALS ENGINEERING AND INDUSTRIAL COMPUTER SCIENCE, 30-059 KRAKÓW, 30 MICKIEWICZA AV., POLAND | |
[2]AMM EUROPE POLAND, ?WIDNICA MANUFACTURING FACILITY | |
关键词: Keywords: 17-4PH grade; Weldability Testing; Copper; Liquid Metal Embrittlement; Stainless Steel; GTAW; Fracture; | |
DOI : 10.2478/v10172-012-0117-1 | |
学科分类:金属与冶金 | |
来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy | |
【 摘 要 】
Problem of welded joint cracking in the HAZ of Cu strengthened 17-4PH grade precipitation hardening martensitic stainless steel is presented. Hypothesis concerning hydrogen embrittlement origin of the cracks is opposed. It was concluded that the cracks located in the high-temperature zone of the HAZ exhibit characteristics of hot cracks which originated as a result of steel embrittlement in the presence of Cu rich liquid phase. The mechanism of steel surface enrichment in Cu is proposed. Practical methods of cracks elimination are presented.【 授权许可】