Hot Deformation Of 6xxx Series Aluminium Alloys

Archives of Metallurgy and Materials

S. Kotowski¹  M. Motyka¹  G. Mrówka-Nowotnik¹  A. Nowotnik¹  J. Sieniawski¹ 

[1] DEPARTMENT OF MATERIALS SCIENCE, RZESZÓW UNIVERSITY OF TECHNOLOGY, W. POLA 2, 35-959 RZESZOW, POLAND

关键词: Keywords: Aluminum alloy;    Hot deformation;    Microstructural evolution;    Activation energy;   

DOI  :  10.1515/amm-2015-0263

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The hot deformation behavior of the 6xxx aluminum alloys was investigated by compression tests in the temperature range 100°C-375°C and strain rate range 10−4s−1 and 4×10−4s−1 using dilatometer DIL 805 BÄHR Thermoanalyse equipped with accessory attachment deformation allows the process to execute thermoplastic in vacuum and inert gas atmosphere. Associated microstructural changes of characteristic states of examined alloys were studied by using the transmission electron microscope (TEM). The results show that the stress level decreases with increasing deformation temperature and deformation rate. And was also found that the activation energy Q strongly depends on both, the temperature and rate of deformation. The results of TEM observation showing that the dynamic flow softening is mainly as the result of dynamic recovery and recrystallization of 6xxx aluminium alloys.

【 授权许可】

Unknown