The Analysis of the High Speed Wire Drawing Process of High Carbon Steel Wires Under Hydrodynamic Lubrication Conditions

Archives of Metallurgy and Materials

M. Suliga¹ 

[1] CZESTOCHOWA UNIVERSITY OF TECHNOLOGY FACULTY OF PRODUCTION ENGINEERING AND MATERIALS TECHNOLOGY INSTITUTE OF METAL FORMING AND SAFETY ENGI-NEERING 19 ARMII KRAJOWEJ STR., 42-200 CZ?STOCHOWA, POLAND;

关键词: Keywords: hydrodynamic dies;    drawing speed;    lubricant conditions;    surface topography;    lubricant pressure;    mechanical properties;   

DOI  :  10.1515/amm-2015-0066

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

In this work the analysis of the wire drawing process in hydrodynamic dies has been done. The drawing process of φ5.5 mm wire rod to the final wire of φ1.7 mm was conducted in 12 passes, in drawing speed range of 5-25 m/s. For final wires of φ1.7 mm the investigation of topography of wire surface, the amount of lubricant on the wire surface and the pressure of lubricant in hydrodynamic dies were determined. Additionally, in the work selected mechanical properties of the wires have been estimated.