Residual Stress Analysis of Insulation Coatings for Magnet Technologies

Archives of Metallurgy and Materials

D. Guney¹ 

[1] YILDIZ TECHNICAL UNIVERSITY, ISTANBUL, TURKEY;

关键词: Keywords: residual stress;    sol-gel;    MgO-ZrO2;    insulation and superconducting magnet;   

DOI  :  10.2478/amm-2013-0053

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

High temperature MgO-ZrO2 insulation coatings were grown on long-length Stainless-Steel (SS) tapes by reel-to-reel sol-gel method for applications of High Temperature Superconductor/Low Temperature Superconductor (HTS/LTS) coils and magnets. The residual stresses were investigated analytically at various temperature ranges, 580°C to 25°C (room temperature) and -196°C (liquid helium temperature), and 630°C to 25°C and -196°C for different thicknesses to be 13, 12, and 7 μm. The maximum stress values were obtained to be 1.92 GPa in tension for SS substrate with the 13 μm coating and -2.42 GPa in compression for the 7 μm MgO-ZrO2 coating in the temperature range between 630°C and liquid helium temperature. The surface morphologies and microstructure of sample were also characterized using a scanning electron microscope (SEM). SEM observations revealed that MgO-ZrO2 coatings have a mosaic like crack structure.

【 授权许可】

Unknown