Effect of the mechanical activation of a talc/kaolin/alumina mixture on the mechanism and kinetics of cordierite formation | |
Moreno, Rodrigo1  Rodrigues Neto, João Batista2  Hotza, Dachamir3  | |
[1] Instituto de Cerámica y Vidrio, Madri, Espanha;Universidade Federal de Santa Catarina, Araranguá, Brasil;Universidade Federal de Santa Catarina, Florianópolis, Brasil | |
关键词: mechanical activation; cordierite; high energy milling.; | |
DOI : 10.5935/0100-4042.20140034 | |
学科分类:化学(综合) | |
来源: Sociedade Brasileira de Quimica | |
【 摘 要 】
In this study, the influence of mechanical activation by intensive ball milling of a stoichiometric mixture of talc, kaolin, and alumina on the mechanism and kinetics of cordierite (2MgO·2Al2O3·5SiO2) formation was evaluated. The raw materials were characterized by chemical analysis, X-ray diffraction (XRD), laser diffraction, and helium pycnometry. The kinetics and mechanism of cordierite formation were studied by XRD, differential thermal analysis, and dilatometry in order to describe the phase formation as a function of temperature (1000-1400 ºC), time of thermochemical treatment (0-4 h), and grinding time of the mixture (0-45 min). Finally, the optimal conditions of the thermochemical treatment that ensured the formation of cordierite were determined: milling time of 45 min and thermal treatment at1280 ºC for 1 h.