Mechanical Assessment of Fire-off on CO/PET Fabrics

18th World Textile Conference

Atakan, Raziye^1 ; Ozcan, Gulay^1

Istanbul Technical University, Faculty of Textile Technologies and Design, Department of Textile Engineering, Gumussuyu, Istanbul

34437, Turkey^1

关键词: After fires;    Fabric samples;    Fabric strength;    Impregnation methods;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/460/1/012052/pdf
DOI  :  10.1088/1757-899X/460/1/012052

来源: IOP

【 摘 要 】

The present study investigates the mechanical properties of newly developed FR chemical Fire-off in order to assess textile service-life features. 350 g/L Fire-off finished bath was prepared and CO/PET fabric samples were treated via impregnation method. In order to investigate FR performance of treated fabrics LOI test was performed. Subsequently, fabric strength, abrasion properties and outward appearance; tensile properties, abrasion, pilling performance and whiteness of Fire-off treated fabrics were tested and evaluated. Mechanical test results showed that there was a slight increase in strength, elongation, abrasion and pilling. On the other hand, whiteness and air permeability of fabrics were decreased after Fire-off treatment.