Modification of ZIF-8 using direct mixing method at a room temperature | |
Mustaqim, A.^1 ; Yuliarto, B.^1,2 ; Nugraha, N.^1,2 | |
Advanced Functional Materials Laboratory, Engineering Physics Department, Bandung Institute of Technology, 10 Ganesha St., Bandung | |
40132, Indonesia^1 | |
Research Center for Nanoscience and Nanotechnology (RCNN), Bandung Institute of Technology, 10 Ganesha St., Bandung | |
40132, Indonesia^2 | |
关键词: Direct mixing method; Hexagonal nanocrystals; Phase purity; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/432/1/012053/pdf DOI : 10.1088/1757-899X/432/1/012053 |
|
来源: IOP | |
【 摘 要 】
ZIF-8 modified with CNT doping have been successfully synthesized using direct mixing methods at room temperature. The characteristics of ZIF-8 and ZIF-8 with CNT were studied using XRD and SEM. The structural integrity and phase purity of both materials were obtained through X-ray diffraction patterns and was found comparable to that of sodalite-type ZIF-8. The peaks were found at 2θ = 7.4°, 16.5°, 22.1°, 25.7°, 26.7°, and 32.53°. When ZIF-8 was doped with CNT, the peaks of ZIF-8 decreased. Scanning electron microscopy of pure ZIF-8 showed hexagonal nanocrystals, and the particle sizes were distributed at approximately 50-140 nm. CNT-doped ZIF-8 showed that ZIF-8 attached to CNT was uniformly with diameters of approximately 80-120 nm. It was concluded that ZIF-8 modified using CNT had been succesfully synthesized.