Analysis of yield locus description on springback behaviour of CR700Y980T-DP steel

International Deep Drawing Research Group 37th Annual Conference

Grubenmann, M.^1 ; Barth, K.^1 ; Heingartner, J.^1 ; Manopulo, N.^2 ; Hora, P.^2 ; Torkabadi, A.^3 ; Van Den Boogaard, T.^3 ; Rösen, H.^4

Inspire- Ivp, Technoparkstrasse 1, Zurich

8005, Switzerland^1

ETH Zurich, Institute of Virtual Manufacturing, Tannenstrasse 3, Zurich

8092, Switzerland^2

University of Twente, Chair Nonlinear Solid Mechanics, P.O. Box 217, AE Enschede

7500, Netherlands^3

Thyssenkrupp Steel Europe AG, Eberhardstrasse 12, Dortmund

44145, Germany^4

关键词: Anisotropic hardenings;    Directional changes;    Identification procedure;    Isotropic hardenings;    Kinematic hardening model;    Material parameter;    Springback prediction;    Stress and strain;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/418/1/012108/pdf
DOI  :  10.1088/1757-899X/418/1/012108

来源: IOP

【 摘 要 】

To precisely predict springback, the stress and strain state has to be described correctly during the forming process and after load removal. In this work, different yield locus descriptions are considered for springback prediction of a CR700Y980T-DP steel with a thickness of 1.5 mm. Experiments and Finite Element Analyses (FEA) with LS-DYNA of a U-bending validation tool were performed and springback predictions compared. In the FEA Hill48, Barlat89 and Barlat's YLD2000 for isotropic hardening, Yoshida-Uemori as a kinematic hardening model and the homogeneous anisotropic hardening (HAH) model are chosen. Monotonic and two-step tensile tests with a directional change of stress are performed and cyclic tension-compression tests are used to determine the material parameters of the investigated hardening models. It is seen that both Yoshida-Uemori and HAH models provide a significant improvement in the springback prediction. The results, however greatly depend on the identification procedure as well as on the modelling of cross-loading contraction effects.