Limit Strain Characterization in an Aluminum Die-Quenching Process

International Deep Drawing Research Group 37th Annual Conference

Dicecco, S.^1 ; Ciano, M. Di^1 ; Butcher, C.^1 ; Worswick, M.^1

University of Waterloo, 200 University Ave W, Waterloo

ON

N2L 3G1, Canada^1

关键词: Aluminum alloy sheet;    D. digital image correlation (DIC);    Elevated temperature;    Non-isothermal condition;    Orange peel defects;    Processing Route;    Quenching process;    Strain distributions;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/418/1/012035/pdf
DOI  :  10.1088/1757-899X/418/1/012035

来源: IOP

【 摘 要 】

This work examines the nature of the strain distributions and limit stains during die quenching of a 7000-series aluminum alloy sheet. Forming limit experiments using limiting dome height (LDH) specimens were performed under plane-strain loading conditions using a 100 mm hemispherical Nakazima punch. Strains were measured using in situ stereoscopic digital image correlation (DIC). Two forming processing routes were examined: (i) an intermediate quench and form (IQF) processing route in which the LDH coupons were solutionized, quenched to a preset temperature, and isothermally formed and (ii) a die-quench (DQ) process where the LDH coupons were solutionized, and quenched and formed simultaneously with room temperature (RT) tooling under non-isothermal conditions. The DQ processing route was devised to understand the formability of the alloy under practical die-quenching conditions, while the IQF route was meant to understand the influence of temperature on the formability of the material. The DQ processing route exhibited the best formability from a localization standpoint; however, it was found that at deformations in excess of 0.5 major true strain, an orange-peel defect was present. The IQF process with room temperature tooling may be comparable to a W-temper forming operation. For these conditions, significant Portevin-Le-Chatelier (PLC) bands were present and the formability was approximately 75% less than for the DQ process. All formability results are summarized and a discussion of the interpretation of forming limits under the diffuse necking conditions associated with elevated temperature forming is presented.