Microstructure evolution of Friction Stir Welded Dissimilar Aerospace Aluminium Alloys | |
机械制造;材料科学 | |
Khan, Noor Zaman^1 ; Siddiquee, Arshad Noor^1 ; Khan, Zahid A.^1 ; Ubaid, Mohammed^1 ; Bajaj, Dhruv^1 ; Atif, Mohd^2 ; Khan, Adnan^2 | |
Department of Mechanical Engineering, Jamia Millia Islamia, New Delhi, India^1 | |
Department of Mechanical Engineering, Integral University Campus, Shahajanhanpur, U.P., India^2 | |
关键词: Aerospace aluminium alloys; Coarser grains; Friction stir; Friction stir welding(FSW); Micro-structure evolutions; Partial recrystallization; Severe plastic deformations; Solid-state joining; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/404/1/012002/pdf DOI : 10.1088/1757-899X/404/1/012002 |
|
学科分类:材料科学(综合) | |
来源: IOP | |
【 摘 要 】
Aluminium alloys exhibiting properties such as high strength to weight ratio, high corrosion resistance etc. has made them a choice for many industrial applications. Therefore, joining of aluminium alloys is of utmost importance, especially for the aerospace industry. Friction stir welding (FSW), a clean novel solid-state joining process, is being used to effectively join dissimilar materials for making different parts of space shuttles, aircrafts etc. 2.5 mm thick dissimilar aluminium alloys, AA2219-O and AA7475-T761, were joined using FSW. Evolution of microstructure for the traverse cross section of welded joint was studied. As a result, significant refinement of grains was observed in stir zone along with dissolution and coagulation of strengthening precipitates due to high rise in temperature and severe plastic deformation. Partial recrystallization was observed in TMAZ along with coarsening of grains and strengthening precipitates. In HAZ, coarser grains and strengthening precipitates was observed with no extent of plastic deformation.