Corrosion Behavior of 45 Steel in Molten Nitrate Salts with 3wt% Impurities at 773.15K | |
Hu, Yongkang^1 ; Han, Yuchen^1 ; Qin, Yiwei^1 ; Zhou, Hongxia^1 | |
Qinghai Provincial Key Laboratory of New Light Alloys, Qinghai Provincial Engineering Research Center of High Performance Light Metal Alloys and Forming, Qinghai University, Xining | |
810016, China^1 | |
关键词: Corrosion behavior; Corrosion kinetics; Corrosion layers; Corrosion mechanisms; Corrosion products; Cross-section morphology; Elements distribution; Gravimetric methods; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/394/3/032117/pdf DOI : 10.1088/1757-899X/394/3/032117 |
|
来源: IOP | |
![]() |
【 摘 要 】
In this paper, the corrosion behavior of 45 steel in molten HitecXL salt (1# salt) and HitecXL salt with 3wt%MgCl2 (2# salt) at 773.15K is studied by gravimetric methods. The cross section characteristics, the elements distribution features and corrosion products of the samples after corrosion are analyzed by SEM, XRD and EDS. The results show that the corrosion kinetics curves of 45 steel for 84 h in 1# and 2# salt all obey the linear law. The cross section morphology show that the corrosion layer depths of the samples are about 10μm and 25μ, respectively. Cl- react with O2 dissolved in the molten salts to form Cl2.then, Cl2 can react with Fe or the oxides of Fe to form FeCl3, which make 45 steel have bigger corrosion rate in 1# salt. The corrosion mechanisms of 45 steel in two kinds of salt are the loss of Fe.【 预 览 】