Reseach on Corrosion Resistance of Solution-treated AZ63D Magnesium Alloy | |
Yin, Yanxiang^1 ; Yang, Guanglei^1 ; Ma, Bojiang^1 | |
Qingdao University of Science and Technology, Qingdao, China^1 | |
关键词: Cast microstructure; Corrosion characteristics; Corrosion current; Corrosion potentials; Corrosion weight loss; Electrochemical measurements; Immersion testing; NaCl solution; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/394/3/032100/pdf DOI : 10.1088/1757-899X/394/3/032100 |
|
来源: IOP | |
![]() |
【 摘 要 】
Theas-cast AZ63D magnesium alloy and its solution-treated microstructure were examined by optical microscopy (OM) and X-ray Diffraction (XRD). The results show that the solution-treated microstructure is more even and the aggregation of β phase is decreased. The immersion testing of AZ63D magnesium alloys exposed to 3.5wt. % NaCl solution and electrochemical measurement were carried out to seek their corrosion characteristics. The results show that the corrosion weight loss of the solution-treated microstructure of AZ63D magnesium alloy is reduced by about 13.01% compared with the theas-cast microstructure. The corrosion resistance of the solution-treated microstructure is obviously better than that of the theas-cast microstructure. The free corrosion potential and the free corrosion current of the solution-treated microstructure is respectively about 2.70% higher and 6.83% less than that of the theas-cast microstructure.【 预 览 】