会议论文详细信息
2018 2nd International Conference on Advanced Technologies in Manufacturing and Materials Engineering | |
Microstructure and Properties of Ni/Al2O3 Composites Prepared by Powder Injection Molding | |
Shang, Feng^1,2,3 ; Cao, Zhenwei^4 ; Zhang, Peng^1 ; Qiao, Bin^1 ; Li, Huaqiang^1 | |
School of Mechanical Engineering, Huaihai Institute of Technology, No.59 Cangwu Road Haizhou District, Lianyungang, Jiangsu | |
222005, China^1 | |
Marine Resources Development Institute of Jiangsu, No.108 Tongguan South Road Haizhou District, Lianyungang, Jiangsu | |
222001, China^2 | |
Jiangsu Key Laboratory of Large Engineering Equipment Detection and Control, Xuzhou Institute of Technology, No.1 Fuchun Road Xincheng District, Xuzhou, Jiangsu | |
221111, China^3 | |
School of Mechanical and Electrical Engineering, China University of Mining and Technology, No.1 Daxue Road, Xuzhou, Jiangsu | |
221116, China^4 | |
关键词: Comprehensive performance; Microstructure and mechanical properties; Microstructure and properties; Powder injection molding; Relative density; Sintering process; Sintering temperatures; Vacuum sintering; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/389/1/012022/pdf DOI : 10.1088/1757-899X/389/1/012022 |
|
来源: IOP | |
【 摘 要 】
Ni/Al2O3 composite was prepared by powder injection molding, the effects of Ni content and different sintering process on the microstructure and mechanical properties of Ni / Al2O3 composites were studied. The results show that when the Ni content is 10%, the comprehensive performance of Ni / Al2O3 composite is better. The optimum vacuum sintering process of 10%Ni / Al2O3 composite is as follows: sintering temperature of 1500 °C for 1 hour, with the relative density of 96.7%, bending strength of 312 MPa, Vickers hardness of 1528HV and fracture toughness of 5.3 MPa•m1/2.