Mechanical and Morphological characterization of Walnut Shell reinforced epoxy composite
机械制造;材料科学;能源学
Lala, S.D.^1 ; Deoghare, A.B.^1 ; Chatterjee, S.^2
Department of Mechanical Engineering, National Institute of Technology Silchar, Silchar
Assam
788010, India^1
Department of Mechanical Engineering, Cooch Behar Government Engineering College, Cooch Behar, West-Bengal
736170, India^2
关键词: Compression modulus;    Filler contents;    Filler materials;    Morphological characterization;    Reinforced epoxy;    SEM micrographs;    Uniform particle distribution;    Weight percentages;   
Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/377/1/012011/pdf
DOI  :  10.1088/1757-899X/377/1/012011
学科分类:材料科学(综合)
来源: IOP
PDF
【 摘 要 】

The present study emphasizes on the development of composite material by reinforcing Walnut Shells (WNS) in Epoxy matrix. Composite material was developed using stir casting process at different weight percentages of Walnut Shell from 0-20. Result from tensile test reveal an improvement of tensile and compression modulus by 20 and 52 % respectively as compared to neat epoxy. However there was a decrease in the tensile and compressive strength. SEM micrograph illustrates that lower filler content result in uniform particle distribution and lesser void formation in the composite which increases with increasing WNS content. However, 1.84 % of water absorption was observed at 5% content which confirm strong encapsulation of filler material by the resin at lower filler wt. content.