Texture Evolution of a 2.8 wt% Si Non-Oriented Electrical Steel during Hot Band Annealing

18th International Conference on Textures of Materials

材料科学;物理学

Mehdi, Mehdi^1,2 ; He, Youliang^1 ; Hilinski, Erik J.^3 ; Edrisy, Afsaneh^2

CanmetMATERIALS, Natural Resources Canada, Hamilton

ON

L8P 0A5, Canada^1

Department of Mechanical, Automotive and Materials Engineering, University of Windsor, Windsor

ON

N9B 3P4, Canada^2

Tempel Steel Co., Chicago

IL

60640-1020, United States^3

关键词: Crystallographic textures;    Electron backscatter diffraction technique;    Evolution of the microstructure;    Hot band annealing;    Non-oriented electrical steel;    Optimal annealing;    Texture evolutions;    Thermo-mechanical processing;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/375/1/012014/pdf
DOI  :  10.1088/1757-899X/375/1/012014

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

To optimize the magnetic properties of non-oriented electrical steels, it is necessary to carefully control all the stages of thermomechanical processing during the production of the steel sheets, since the microstructure and crystallographic texture at an early step will usually affect those at the subsequent steps. Many studies have shown that hot band annealing may have a positive effect on the texture of the final sheet, but it is not clear what are the optimal annealing conditions to obtain the desired final textures. In this study, the evolution of microtexture and microstructure of a 2.8 wt% Si non-oriented electrical steel during hot band annealing is studied by using electron backscatter diffraction (EBSD) techniques. A region of the hot-rolled sample was marked by micro-indents so that the same area could be examined at various annealing times (under the same temperature) to investigate the evolution of the microstructure and microtexture during recrystallization. In this way, the mechanisms of texture evolution was elucidated, and optimal annealing conditions can be determined.