Comparison of rolling texture of austenite and ferrite phases of duplex steel with single-phase austenitic and ferritic steel

18th International Conference on Textures of Materials

材料科学;物理学

Capek, J.^1 ; Cernik, M.^2 ; Ganev, N.^1 ; Trojan, K.^1 ; Nemecek, J.^1 ; Kolarik, K.^1

Department of Solid State Engineering, Faculty of Nuclear Sciences and Physical Engineering, Czech Technical University in Prague, Trojanova 13, Prague, Czech Republic^1

U. S. Steel Koice S.r.o., Koice, Slovakia^2

关键词: Duplex steels;    Electron back-scattered diffraction;    Kurdjumov-sachs orientation relationships;    Mechanical and thermal properties;    Preferred orientations;    Rolled steel plates;    Rolling texture;    Texture components;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/375/1/012025/pdf
DOI  :  10.1088/1757-899X/375/1/012025

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

In this contribution, the behavior of three types of steel after rolling was investigated. Ferritic and austenitic steels or phases have different mechanical and thermal properties. Due to their mutual influence during plastic deformation, it is possible to suppose the differences between preferred orientations of austenite and ferrite phases in duplex steel and single-phase austenitic and ferritic steels. For this reason, the preferred orientations of austenite and ferrite phases of rolled duplex steel were compared with rolled single-phase austenitic and ferritic steel. The 0-50% reductions of rolled steel plates were selected. Mainly, the strength and type of preferred orientation were compared in the relation to reduction and material. For this purpose, the rolled surfaces were measured by X-ray diffraction. The significant differences between intensities and types of texture components were investigated. For austenite-ferrite interaction during plastic deformation and phase transformation, samples were analysed by electron back-scattered diffraction. The Kurdjumov-Sachs orientation relationship was investigated.