Magnetic Properties of Rapid Cooled FeCoB Based Alloys Produced by Injection Molding | |
Nabialek, M.^1 ; Jez, B.^1 ; Jez, K.^1 ; Pietrusiewicz, P.^1 ; Gruszka, K.^1 ; Bloch, K.^1 ; Gondro, J.^1 ; Rzacki, J.^1 ; Abdullah, M.M.A.B.^2 ; Sandu, A.V.^3 ; Szota, M.^4 | |
Institute of Physics, Faculty of Production Engineering and Materials Technology, Czestochowa University of Technology, 19 Armii Krajowej Str., Czestochowa | |
42-200, Poland^1 | |
Gheorghe Asachi Technical University of Iasi, Faculty of Materials Science and Engineering, 41 D. Mangeron Blvd., Iasi | |
700115, Romania^2 | |
Geopolymer and Green Technology (CeGeoGTech), School of Material Engineering, Universiti Malaysia Perlis (UniMAP), Kangar, Perlis | |
01000, Malaysia^3 | |
Institute of Materials Engineering, Faculty of Production Engineering and Materials Technology, Czestochowa University of Technology, 19 Armii Krajowej Str., Czestochowa | |
42-200, Poland^4 | |
关键词: Coercive field; Copper molds; Crystalline phasis; Liquid alloy; Magnetic balance; Magnetization of saturation; Thick plate; X ray diffractometers; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/374/1/012021/pdf DOI : 10.1088/1757-899X/374/1/012021 |
|
来源: IOP | |
【 摘 要 】
The paper presents the results of investigations of the structure and magnetic properties of massive rapid cooled Fe50-xCo20+xB20Cu1Nb9alloys (where x = 0, 5). Massive alloys were made using the method of injecting a liquid alloy into a copper mold. Samples were obtained in the form of 0.5 mm thick plates. The structure of the obtained samples was examined using an X-ray diffractometer equipped with a CuKα lamp. The phase composition of the alloys formed was determined using the Match program. By using Sherrer's dependence the grain sizes of the identified crystalline phases were estimated. Using the Faraday magnetic balance, the magnetization of samples as a function of temperature in the range from room temperature to 850K was measured. Magnetization of saturation and value of the coercive field for the prepared alloys were determined on the basis of magnetic hysteresis loop measurement using the LakeShore vibration magnetometer.