Electroplating of aluminium microparticles with nickel to synthesise reactive core-shell structures for thermal joining applications

20th Chemnitz Seminar on Materials Engineering - 20. Werkstofftechnisches Kolloquium

Schreiber, S.^1 ; Zaeh, M.F.^1

Institute for Machine Tools and Industrial Management (Iwb), Technical University of Munich, Boltzmannstrasse 15, Garching

85748, Germany^1

关键词: Aluminium microparticles;    Aluminium particles;    Core shell structure;    Electroless process;    Electroplating process;    Experimental set up;    Process parameters;    Reactive particles;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/373/1/012008/pdf
DOI  :  10.1088/1757-899X/373/1/012008

来源: IOP

【 摘 要 】

Reactive particles represent a promising alternative for effectively joining components with freeform surfaces and different material properties. While the primary application of reactive systems is combustion synthesis for the production of high-performance alloys, the highly exothermic reaction can also be used to firmly bond thermosensitive joining partners. Core-shell structures are of special interest, since they function as separate microreactors. In this paper, a method to synthesise reactive nickel-aluminium core-shell structures via a two-step plating process is described. Based on an electroless process, the natural oxide layer of the aluminium particles is removed and substituted with a thin layer of nickel. Subsequently, the pre-treated particles are electroplated with nickel. The high reactivity of aluminium and the oxide layer play a significant role in adjusting the process parameters of the Watts bath. Additionally, the developed experimental set-up is introduced and the importance of process control is shown. In order to achieve reproducible results, the electroplating process was automated. Ignition tests with electromagnetic waves demonstrated that the particles undergo an exothermic reaction. Therefore, they can be used as a heat source in thermal joining applications.