The Effect of Nano Loading and Ultrasonic Compounding of EVA/LDPE/Nano-magnesium Hydroxide on Mechanical Properties and Distribution of Nano Particles

3rd International Conference on Global Sustainability and Chemical Engineering

工业技术;化学工业

Azman, I.A.^1 ; Salleh, R.M.^1 ; Alauddin, S.M.^1 ; Shueb, M.I.^2

Faculty of Chemical Engineering, Universiti Teknologi MARA (UiTM), Selangor, Shah Alam, Malaysia^1

Agensi Nuklear Malaysia, Bangi, Selangor, Malaysia^2

关键词: Dispersion of nano particles;    Environmental stress crackings;    Ethylene vinyl acetates;    Fire-resistant properties;    Low Density Polyethylene (LDPE);    Magnesium hydroxide;    Ultrasonic technology;    Wire and cable industry;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/358/1/012062/pdf
DOI  :  10.1088/1757-899X/358/1/012062

学科分类：工业工程学

来源: IOP

【 摘 要 】

Blends of Ethylene Vinyl Acetate (EVA) and Low-Density Polyethylene (LDPE) are promising composite which have good mechanical properties to environmental stress cracking. However, they lack fire resistant properties, which limits it usage in wire and cable industry. In order to improve flame retardancy ability, a range of nano-magnesium hydroxide (nano-MH) loading which is from 0 phr to maximum of 20 phr with ultrasonic extrusion 0-100 kHz frequencies have been introduced. Ultrasonic extrusion was used to improve the distribution of nano-MH. It was found that, 10 phr of nano loading with 100 kHz ultrasonic assisted has greater tensile strength compared to the nanocomposite without ultrasonication. Further increase of nano MH loading, will decrease the tensile properties. Better elongation at break was observed at10 phr nano-MH with the frequency of 50 kHz. The sample of 20 phr of nanoMH assisted with 50 kHz ultrasonic exhibits good flexural properties while 10 phr of nano-MH without the ultrasonic assisted demonstrates good in izod impact properties. From the evaluation of mechanical properties studied, it was found that 10 phr of nano-MH has shown the best performance among all the samples tested for EVA/LDPE/nano-MH composites. Transmission Electron Microscopy (TEM) has been conducted on 10 phr sample with different frequencies in order to observe the distribution of nano-MH particles. The sample with 100 kHz frequency shows more uniform dispersion of nano-MH in EVA/LDPE composites. This investigation indicates that the ultrasonic technology can enhance the mechanical properties studied as well as the dispersion of nano particles in the composite.