Thermal shock effect on Mechanical and Physical properties of pre-moisture treated GRE composite

7th National Conference on Processing and Characterization of Materials

Chakraverty, A.P.^1 ; Panda, A.B.^1 ; Mohanty, U.K.^2,3 ; Mishra, S.C.^2 ; Biswal, B.B.^4

Department of Physics, C. V. Raman College of Engineering, Bhubaneswar, Odisha

752054, India^1

Department of Metallurgical and Materials Engineering, National Institute of Technology, Rourkela, Odisha

769008, India^2

Department of Mechanical Engineering, Institute of Technical and Educational Research (ITER), SOA University, Bhubaneswar, Odisha

751030, India^3

National Institute of Technology, Maghalaya, Meghalaya

793003, India^4

关键词: Glass fibre reinforced;    Glass fibre reinforced polymers;    ILSS;    Inter-laminar shear strengths;    Mechanical and physical properties;    Temperature fluctuation;    Thermal shock effect;    Thermo-mechanical degradation;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/338/1/012047/pdf
DOI  :  10.1088/1757-899X/338/1/012047

来源: IOP

【 摘 要 】

Many practical situations may be encountered under which a GFRP (Glass fibre reinforced polymer) composite, during its service life, is exposed to the severities of sudden temperature fluctuations. Moisture absorption of GRE (Glass fibre reinforced epoxy) composites followed by various gradients of temperature fluctuations may cause thermo- mechanical degradation. It is on this context, the hand layed GRE composite samples are exposed to up-thermal shock (-40°C to +50°C) and down-thermal shock (+50°C to -40°C) for various time interval after several periods of moisture (hydrothermal/hygrothermal) conditioning. The thermally shocked GRE specimens are put to 3-point bend test to divulge inter laminar shear strength (ILSS). Least ILSS values are recorded for the samples with maximum period of moisture treatments under with both up-thermal and down-thermal shock conditions. Lower glass transition temperature (Tg) values, as revealed through the low temperature DSC test, are exhibited at maximum durations of both up-thermal and down-thermal shock for the samples with higher periods of hygrothermal/hydrothermal treatments. SEM fractographs of representative GRE specimens after optimum period of moisture treatments and thermal shock show the various modes of failures.