Sea water Corrosion of Nickel based Plasma Spray Coating | |
Parida, M.^1 ; Nanda, S.P.^1 ; Bhuyan, S.K.^2 ; Mishra, S.C.^2 | |
Dept. of Chemistry, CUTM, Odisha, India^1 | |
Department of MandME, N.I.T, Rourkela, India^2 | |
关键词: Coating morphology; Deposited materials; Erosion resistant coatings; Nickel-base; Nickel-based coatings; Plasma spray coating; Thermal plasma; Working temperatures; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/338/1/012051/pdf DOI : 10.1088/1757-899X/338/1/012051 |
|
来源: IOP | |
【 摘 要 】
Different types of erosion resistant coatings are applied/deposited on aero components, depending on the operating/working temperatures. Nickel based coating are applied on the air craft (compressor) components, which can sustain up to working temperature of 650°C. In the present investigation, to improve the compatibility between substrate (i.e. the machine component) and the top coat, application of bond coat is there. The application of Nickel based coating by thermal plasma spray technique has proven to be a satisfactory means of producing acceptable sealing surface with excellent abradability. Before the corrosion study, coated sample is subjected to hardness, thickness and porosity testing. Hence the result is being evaluated. The corrosion behavior of coating was studied by sea water immersion with a time period of 16 weeks. It is observed that, up to 9 weeks increase in weight of coating occurs in a sharp trend and then takes a decreasing trend. The weight gain of the samples has varied from 37.23% (with one week immersion in sea water) to a maximum of about 64.36% for six weeks immersion. Coating morphology and composition analysis of the coatings are studied using SEM and EDS. This behavior shows adsorption/deposition of the foreign particles with polygonal shape on the coating surface by sea water interaction. Foreign particles with polygonal shape deposited on the coating and with increase in immersion/treatment time, washing out of the deposited materials starts, which reflects the decreasing trend of weight gain of the specimen.