Experimental and numerical investigations on the temperature distribution in PVD AlTiN coated and uncoated Al2O3/TiCN mixed ceramic cutting tools in hard turning of AISI 52100 steel

7th National Conference on Processing and Characterization of Materials

Kumar, Ch Sateesh^1 ; Patel, Saroj Kumar^1 ; Das, Anshuman^1

Department of Mechanical Engineering, National Institute of Technology, Rourkela Odisha, India^1

关键词: Coated cutting tools;    Coefficient of frictions;    Comparative assessment;    Cutting temperature;    Elevated temperature;    Infrared thermometers;    Measured temperatures;    Numerical investigations;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/338/1/012021/pdf
DOI  :  10.1088/1757-899X/338/1/012021

来源: IOP

【 摘 要 】

Temperature generation in cutting tools is one of the major causes of tool failure especially during hard machining where machining forces are quite high resulting in elevated temperatures. Thus, the present work investigates the temperature generation during hard machining of AISI 52100 steel (62 HRC hardness) with uncoated and PVD AlTiN coated Al2O3/TiCN mixed ceramic cutting tools. The experiments were performed on a heavy duty lathe machine with both coated and uncoated cutting tools under dry cutting environment. The temperature of the cutting zone was measured using an infrared thermometer and a finite element model has been adopted to predict the temperature distribution in cutting tools during machining for comparative assessment with the measured temperature. The experimental and numerical results revealed a significant reduction of cutting zone temperature during machining with PVD AlTiN coated cutting tools when compared to uncoated cutting tools during each experimental run. The main reason for decrease in temperature for AlTiN coated tools is the lower coefficient of friction offered by the coating material which allows the free flow of the chips on the rake surface when compared with uncoated cutting tools. Further, the superior wear behaviour of AlTiN coating resulted in reduction of cutting temperature.