Bioplastic from Chitosan and Yellow Pumpkin Starch with Castor Oil as Plasticizer

International Conference on Advanced Materials for Better Future 2017

Hasan, M.^1 ; Rahmayani, R.F.I.^1 ; Munandar^1

Department of Chemistry Education, Faculty of Teacher Training and Education, Syiah Kuala University, Darussalam Banda Aceh

23111, Indonesia^1

关键词: Absorption capacity;    Biodegradation rate;    Biodegradation test;    Bioplastics;    Castor oil;    Cucurbita moschata;    Solvent absorption;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/333/1/012087/pdf
DOI  :  10.1088/1757-899X/333/1/012087

来源: IOP

【 摘 要 】

This study has been conducted on bioplastic synthesis of chitosan and yellow pumpkin starch (Cucurbita moschata) with castor oil as plasticizer. The purpose of this study is to determine the characteristics of the effect of chitosan and starch composition of pumpkins against solvent absorption, tensile strength and biodegradable. The first stage of the research is the making of bioplastic by blending yellow pumpkin starch, chitosan and castor oil. Further, it tested the absorption capacity of the solvent, tensile strength test, and biodegradable analysis. The optimum absorption capacity of the solvent is obtained on the composition of Pumpkin/Chitosan was 50/50 in H2O and C2H5OH solvent. Meanwhile the optimum absorbency in HCl and NaOH solvents is obtained by 60/40 composition. The characterization of the optimum tensile strength test was obtained on the 40/60 composition of 6.787 ± 0.274 Mpa and the fastest biodegradation test process within 5-10 days occurred in the 50/50 composition. The more chitosan content the higher the value of tensile strength test obtained, while the fastest biodegradation rate occureds in the composition of yellow pumpkin starch and chitosan balanced 50:50.