Effect of FSW welding speed on microstructure and microhardness of Al-0.84Mg-0.69Si-0.76Fe alloy at moderate rotational tool velocity

International Conference on Recent Advances in Materials, Mechanical and Civil Engineering

材料科学;机械制造;土木建筑工程

Chand, Suresh^1 ; Vineetha, S.^1 ; Madhusudhan, D.^1 ; Sai Krishna, C.H.^1 ; Kusuma Devi, G.^1 ; Bhawani^1 ; Hemarao, K.^1 ; Ganesh Naidu, G.^1

Department of Metallurgical and Materials Engineering, RGUKT IIIT Nuzvid, AP, India^1

关键词: Double sides;    Fine microstructure;    FSW welding;    Rotational tools;    Rotational velocity;    Stir zones;    Thermomechanically affected zones;    Welding speed;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/330/1/012022/pdf
DOI  :  10.1088/1757-899X/330/1/012022

来源: IOP

【 摘 要 】

The plate of 7.0 mm thickness was double side welded using friction stir welding is investigated. The rotational velocity of friction stir welding tool is used 1400 rpm. The influence of welding speed on the microstructure and microhardness values of Al-0.84Mg-0.69Si-0.76Fe aluminum alloy is presented. Two welding speeds 25 mm/min and 31.5 mm/min are used. The microhardness values of friction stir weld are measured at various locations from the weld interface. The microhardness values in stir zone of weld are found larger than lower welding speed at constant rotational velocity of 1400 rpm of friction stir welding tool. The similar effects on microhardness values are found in the thermo-mechanically affected zone and heat affected zone. The fine microstructure is observed at 31.5 mm/min welding speed compared to the 25 mm/min welding speed at 1400 rpm.