Plasma carburizing with surface micro-melting

International Conference on Mechanical Engineering, Automation and Control Systems 2017

机械制造;无线电电子学;计算机科学

Balanovsky, A.E.^1 ; Grechneva, M.V.^1 ; Van Huy, Vu^1 ; Ponomarev, B.B.^1

Irkutsk National Research Technical University, 83 Lermontov St., Irkutsk

664074, Russia^1

关键词: Distribution profiles;    Graphite coatings;    Graphite powder;    Plasma carburizing;    Plasma surfaces;    Plasma treatment;    Processing parameters;    Resistance properties;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/327/4/042010/pdf
DOI  :  10.1088/1757-899X/327/4/042010

学科分类：计算机科学（综合）

来源: IOP

【 摘 要 】

This paper presents carburizing the surface of 20 low carbon steel using electric arc and graphite prior. A carbon black solution was prepared with graphite powder and sodium silicate in water. A detailed analysis of the phase structure and the distribution profile of the sample hardness after plasma treatment were given. The hardened layer consists of three different zones: 1-the cemented layer (thin white zone) on the surface, 2-heat-affected zone (darkly etching structure), 3-the base metal. The experimental result shows that the various microstructures and micro-hardness profiles were produced depending on the type of graphite coating (percentage of liquid glass) and processing parameters. The experiment proved that the optimum content of liquid glass in graphite coating is 50-87.5%. If the amount of liquid glass is less than 50%, adhesion to metal is insufficient. If liquid glass content is more than 87.5%, carburization of a metal surface does not occur. A mixture of the eutectic lamellar structure, martensite and austenite was obtained by using graphite prior with 67% sodium silicate and the levels of the hardness layer increased to around 1000 HV. The thickness of the cemented layer formed on the surface was around 200 μm. It is hoped that this plasma surface carburizing treatment could improve the tribological resistance properties.