会议论文详细信息
2017 International Symposium on Application of Materials Science and Energy Materials | |
Stress Corrosion Cracking Behavior of LD10 Aluminum Alloy in UDMH and N2O4 propellant | |
材料科学;能源学 | |
Zhang, Youhong^1 ; Chang, Xinlong^1 ; Liu, Wanlei^1 | |
Xi'An Research Institute of Hi-tech, Xi'an, China^1 | |
关键词: 3.5% nacl; Corrosion environments; Crack propagation behavior; Dinitrogen; Double cantilever beam; LD10 aluminum alloys; Stress corrosion; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/322/2/022058/pdf DOI : 10.1088/1757-899X/322/2/022058 |
|
学科分类:材料科学(综合) | |
来源: IOP | |
【 摘 要 】
The LD10 aluminum alloy double cantilever beam specimens were corroded under the conditions of Unsymmetric Uimethyl Hydrazine (UDMH), Dinitrogen Tetroxide (N2O4), and 3.5% NaCl environment. The crack propagation behavior of the aluminum alloy in different corrosion environment was analyzed. The stress corrosion cracking behavior of aluminum alloy in N2O4is relatively slight and there are not evident stress corrosion phenomenons founded in UDMH.