Textile Dye Removal from Aqueous Solution using Modified Graphite Waste/Lanthanum/Chitosan Composite

Quality in Research: International Symposium on Materials, Metallurgy, and Chemical Engineering

材料科学;冶金学;化学工业

Kusrini, E.^1 ; Wicaksono, B.^1 ; Yulizar, Y.^2 ; Prasetyanto, E.A.^3 ; Gunawan, C.^4

Department of Chemical Engineering, Faculty of Engineering, Universitas Indonesia, Kampus Baru UI, Depok

16424, Indonesia^1

Department of Chemistry, Faculty of Mathematics and Natural Sciences, Universitas, Kampus Baru UI, Depok

16424, Indonesia^2

Faculty of Medicine, Atma Jaya Catholic University of Indonesia, Jakarta

14440, Indonesia^3

Ithree Institute, University of Technology Sydney, Sydney

NSW

2007, Australia^4

关键词: Adsorbent materials;    Adsorption efficiency;    Adsorption performance;    Experimental conditions;    Lanthanum concentrations;    Mechanical crushing;    Pretreatment process;    Selective adsorption;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/316/1/012029/pdf
DOI  :  10.1088/1757-899X/316/1/012029

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

We investigated various pre-treatment processes of graphite waste using thermal, mechanical and chemical methods. The aim of this work is to study the performance of modified graphite waste/lanthanum/chitosan composite (MG) as adsorbent for textile dye removal from aqueous solution. Effect of graphite waste resources, adsorbent size and lanthanum concentration on the dye removal were studied in batch experiments. Selectivity of MG was also investigated. Pre-heated graphite waste (NMG) was conducted at 80°C for 1 h, followed by mechanical crushing of the resultant graphite to 75 μm particle size, giving adsorption performance of ∼58%, ∼67%, ∼93% and ∼98% of the model dye rhodamine B (concentration determined by UV-vis spectroscopy at 554 nm), methyl orange (464 nm), methylene blue (664 nm) and methyl violet (580 nm), respectively from aqueous solution. For this process, the system required less than ∼5 min for adsorbent material to be completely saturated with the adsorbate. Further chemical modification of the pre-treated graphite waste (MG) with lanthanum (0.01 - V 0.03 M) and chitosan (0.5% w/w) did not improve the performance of dye adsorption. Under comparable experimental conditions, as those of the 'thermal-mechanical-pre-treated-only' (NMG), modification of graphite waste (MG) with 0.03 M lanthanum and 0.5% w/w chitosan resulted in ∼14%, ∼47%, ∼72% and ∼85% adsorption of rhodamine B, methyl orange, methylene blue and methyl violet, respectively. Selective adsorption of methylene blue at most to ∼79%, followed by methyl orange, methyl violet and rhodamine B with adsorption efficiency ∼67, ∼38, and ∼9% sequentially using MG with 0.03 M lanthanum and 0.5% w/w chitosan.